Cmos semiconductor device and method for manufacturing the same

ABSTRACT

A CMOS semiconductor device having an n-type MOSFET and a p-type MOSFET, comprising: a gate electrode of the n-type MOSFET having a first insulation layer composed of a high-k material, and a first metal layer provided on the first insulation layer and composed of a metal material; and a gate electrode of the p-type MOSFET having a second insulation layer composed of a high-k material, and a second metal layer provided on the second insulation layer and composed of a metal material, wherein the first insulation layer and the second insulation layer are composed of the different high-k materials, and the first metal layer and the second metal layer are composed of the same metal material.

TECHNICAL FIELD

The present invention relates to a CMOS semiconductor device and a method for producing the same, and more particularly to a CMOS semiconductor device using a high-k material for a gate electrode and a method for producing the same.

BACKGROUND ART

Recently, as a CMOS semiconductor device is miniaturized, what is troubling is that a gate insulation layer composed of SiON or SiO₂ becomes thin and a leak current goes through the gate insulation layer due to a tunneling phenomenon.

To solve this problem, a high-k material (high-dielectric material) such as hafnium is used for the gate insulation layer and a thickness of the gate insulation layer is set to a constant value to prevent the leak current from being generated. In addition, when the high-k material is used for a gate electrode, Fermi level pinning is generated at a boundary with a silicon gate electrode, so that as a gate electrode material, a metal such as nickel silicide is used instead of polycrystalline silicon.

For example, when the high-k material is used for the gate insulation layer, NiSi is used for a metal gate electrode of a p-channel MOSFET, and Ni₂Si is used for a metal gate electrode of an n-channel MOSFET.

Patent document 1: Japanese Unexamined Patent Publication No. 2002-359295

DISCLOSURE OF THE INVENTION Problems to be Solved by the Invention

In the CMOS semiconductor device, it is necessary to control a gate length Lg with a high degree of accuracy to control threshold voltages of the p-channel MOSFET and the n-channel MOSFET. When the gate length Lg is 20 nm, for example, allowable LWR (Line Width Roughness) of the gate length is about 5%, which means about 1 nm.

However, the gate electrodes composed of different materials such as NiSi and Ni₂Si cannot be processed with a high degree of accuracy in the same etching step, that is, in one etching step using one kind of etching gas, so that a side wall of the electrode is tapered in general.

On the other hand, when the two gate electrodes composed of different materials are processed in different etching steps, etching masks cannot be aligned due to a fine structure in which the gate length Lg is as small as 20 nm.

Thus, it is an object of the present invention to provide a CMOS semiconductor device capable of controlling a gate length with a high degree of accuracy in the CMOS semiconductor device using a high-k material, and a production method for producing the same.

Means for Solving the Problem

Therefore, the present invention is a CMOS semiconductor device having an n-type MOSFET and a p-type MOSFET, comprising: a gate electrode of the n-type MOSFET having a first insulation layer composed of a high-k material, and a first metal layer provided on the first insulation layer and composed of a metal material; and a gate electrode of the p-type MOSFET having a second insulation layer composed of a high-k material, and a second metal layer provided on the second insulation layer and composed of a metal material, wherein the first insulation layer and the second insulation layer are composed of the different high-k materials, and the first metal layer and the second metal layer are composed of the same metal material.

Furthermore, the present invention is a method for producing a CMOS semiconductor device having an n-type MOSFET and a p-type MOSFET, comprising the steps of: preparing a semiconductor substrate defined by an n-type MOSFET formation region and a p-type MOSFET formation region; forming a high-k material layer, a first cap layer, and a first metal layer, sequentially on the semiconductor substrate; removing the first cap layer and the first metal layer except for those in the p-type MOSFET formation region; forming a second cap layer and a second metal layer, sequentially on the semiconductor substrate; removing the second metal layer except for that in the n-type MOSFET formation region; removing the second cap layer provided between the n-type MOSFET formation region and the p-type MOSFET formation region, using the first metal layer and the second metal layer as masks; removing the first metal layer and the second metal layer; forming a gate metal material layer on the semiconductor substrate; and forming a gate metal layer of a gate electrode of each of the n-type MOSFET and the p-type MOSFET by etching the gate metal material layer in the same etching step.

EFFECT OF THE INVENTION

The CMOS semiconductor device according to the present invention can control a threshold voltage with a high degree of accuracy.

In addition, according to the method for producing a CMOS semiconductor device in the present invention, since the gate metal layer of the gate electrode each of the n-type MOSFET and the p-type MOSFET can be formed in the same etching step, the gate electrode can be processed with a high degree of accuracy.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a cross-sectional view of a CMOS semiconductor device according to a first embodiment.

FIG. 1A is a cross-sectional view of a production step of the CMOS semiconductor device according to the first embodiment.

FIG. 1B is a cross-sectional view of a production step of the CMOS semiconductor device according to the first embodiment.

FIG. 1C is a cross-sectional view of a production step of the CMOS semiconductor device according to the first embodiment.

FIG. 1D is a cross-sectional view of a production step of the CMOS semiconductor device according to the first embodiment.

FIG. 1E is a cross-sectional view of a production step of the CMOS semiconductor device according to the first embodiment.

FIG. 1F is a cross-sectional view of a production step of the CMOS semiconductor device according to the first embodiment.

FIG. 1G is a cross-sectional view of a production step of the CMOS semiconductor device according to the first embodiment.

FIG. 1H is a cross-sectional view of a production step of the CMOS semiconductor device according to the first embodiment.

FIG. 1I is a cross-sectional view of a production step of the CMOS semiconductor device according to the first embodiment.

FIG. 1J is a cross-sectional view of a production step of the CMOS semiconductor device according to the first embodiment.

FIG. 1K is a cross-sectional view of a production step of the CMOS semiconductor device according to the first embodiment.

FIG. 2A is a cross-sectional view of a production step of a CMOS semiconductor device according to a second embodiment.

FIG. 2B is a cross-sectional view of a production step of the CMOS semiconductor device according to the second embodiment.

FIG. 2C is a cross-sectional view of a production step of the CMOS semiconductor device according to the second embodiment.

FIG. 3A is a cross-sectional view of a production step of a CMOS semiconductor device according to a third embodiment.

FIG. 3B is a cross-sectional view of a production step of the CMOS semiconductor device according to the third embodiment.

FIG. 3C is a cross-sectional view of a production step of the CMOS semiconductor device according to the third embodiment.

FIG. 3D is a cross-sectional view of a production step of the CMOS semiconductor device according to the third embodiment.

FIG. 3E is a cross-sectional view of a production step of the CMOS semiconductor device according to the third embodiment.

FIG. 3F is a cross-sectional view of a production step of the CMOS semiconductor device according to the third embodiment.

FIG. 3G is a cross-sectional view of a production step of the CMOS semiconductor device according to the third embodiment.

FIG. 3H is a cross-sectional view of a production step of the CMOS semiconductor device according to the third embodiment.

FIG. 4A is a cross-sectional view of a production step of a CMOS semiconductor device according to a fourth embodiment.

FIG. 4B is a cross-sectional view of a production step of the CMOS semiconductor device according to the fourth embodiment.

FIG. 4C is a cross-sectional view of a production step of the CMOS semiconductor device according to the fourth embodiment.

FIG. 4D is a cross-sectional view of a production step of the CMOS semiconductor device according to the fourth embodiment.

FIG. 4E is a cross-sectional view of a production step of the CMOS semiconductor device according to the fourth embodiment.

FIG. 4F is a cross-sectional view of a production step of the CMOS semiconductor device according to the fourth embodiment.

FIG. 4G is a cross-sectional view of a production step of the CMOS semiconductor device according to the fourth embodiment.

FIG. 4H is a cross-sectional view of a production step of the CMOS semiconductor device according to the fourth embodiment.

FIG. 5A, is a cross-sectional view of a production step of another CMOS semiconductor device according to the fourth embodiment.

FIG. 5B is a cross-sectional view of a production step of another CMOS semiconductor device according to the fourth embodiment.

FIG. 5C is a cross-sectional view of a production step another CMOS semiconductor device according to the fourth embodiment.

FIG. 6A is a cross-sectional view of a production step of a CMOS semiconductor device according to a fifth embodiment.

FIG. 6B is a cross-sectional view of a production step of the CMOS semiconductor device according to the fifth embodiment.

FIG. 6C is a cross-sectional view of a production step of the CMOS semiconductor device according to the fifth embodiment.

FIG. 6D is a cross-sectional view of a production step of the CMOS semiconductor device according to the fifth embodiment.

FIG. 6E is a cross-sectional view of a production step of the CMOS semiconductor device according to the fifth embodiment.

FIG. 6F is a cross-sectional view of a production step of the CMOS semiconductor device according to the fifth embodiment.

FIG. 6G is a cross-sectional view of a production step of the CMOS semiconductor device according to the fifth embodiment.

FIG. 6H is a cross-sectional view of a production step of the CMOS semiconductor device according to the fifth embodiment.

FIG. 7A is a cross-sectional view of a production step of a CMOS semiconductor device according to a sixth embodiment.

FIG. 7B is a cross-sectional view of a production step of the CMOS semiconductor device according to the sixth embodiment.

FIG. 7C is a cross-sectional view of a production step of the CMOS semiconductor device according to the sixth embodiment.

FIG. 7D is a cross-sectional view of a production step of the CMOS semiconductor device according to the sixth embodiment.

FIG. 7E is a cross-sectional view of a production step of the CMOS semiconductor device according to the sixth embodiment.

FIG. 7F is a cross-sectional view of a production step of the CMOS semiconductor device according to the sixth embodiment.

FIG. 8 is a structural drawing of gate electrodes of a CMOS semiconductor device according to a seventh embodiment.

FIG. 9 is a structural drawing of gate electrodes of the CMOS semiconductor device described in the first to sixth embodiments.

FIG. 10A is a schematic view of a production step of a CMOS semiconductor device according to an eighth embodiment.

FIG. 10B is a schematic view of a production step of the CMOS semiconductor device according to the eighth embodiment.

FIG. 11 is a structural drawing of gate electrodes of a CMOS semiconductor device according to a ninth embodiment.

EXPLANATION OF REFERENCES

1, 11, 21 . . . insulation layer, 12, 22 . . . cap layer, 13, 14, 23, 24 . . . metal layer, 10, 20 . . . gate electrode, 100 . . . CMOS semiconductor device, 101 . . . n-type MOSFET, 102 . . . p-type MOSFET, 105 . . . semiconductor substrate, 110 . . . n-well region, 120 . . . p-well region, 111, 121 . . . gate/source regions, 130 . . . element isolation layer

BEST MODE FOR CARRYING OUT THE INVENTION

Hereinafter, preferred embodiments of the present invention will be described with reference to the drawings. In addition, while “upper”, “lower”, “left” and “right”, and names including these terms are occasionally used in the following descriptions, these directions are used to easily understand the present invention with reference to the drawings, so that a configuration where the embodiment is vertically inverted or rotated in a certain direction may be included in the technical scope of the present invention as a matter of course.

First Embodiment

FIG. 1 is a cross-sectional view of a CMOS semiconductor device (complementary metal oxide semiconductor device) represented by 100 as a whole according to a first embodiment.

The CMOS semiconductor device 100 includes an n-type MOSFET 101 and a p-type MOSFET 102.

The CMOS semiconductor device 100 includes a semiconductor substrate 105 composed of silicon, for example. An n-type well region 110 and a p-type well region 120 are provided in the semiconductor substrate 100. The n-type well region 110 and the p-type well region 120 are insulated by an interlayer insulation layer 130 composed of silicon oxide, for example.

Source/drain regions 111 are provided in the n-type well region 110. A gate electrode 10 is provided on a channel region sandwiched between the source/drain regions 111. The gate electrode 10 includes a gate insulation layer 11, a cap layer 12, and gate metal layers 13 and 14 provided thereon. The gate insulation layer 11 is composed of a high-k material such as HfLaO or HfMgO, and the cap layer 12 is composed of MgO or LaO, for example. In addition, the gate metal layer 13 is composed of a mid-gap material having high heat resistance such as TiN, TaN, TaSiN, NiSi, PtSi, or CoSi₂, and the gate metal layer 14 is made of a low resistance material such as W.

Meanwhile, source/drain regions 121 are provided in the p-type well region 120. A gate electrode 20 is provided on a channel region sandwiched between the source/drain regions 121. The gate electrode 20 includes a gate insulation layer 21, a cap layer 22, and gate metal layers 23 and 24 provided thereon. The gate insulation layer 21 is composed of a high-k material such as HfAlO, and the cap layer 22 is composed of AlO, for example. In addition, the gate metal layers 23 and 24 are composed of the same materials as those of the gate metal layers 13 and 14 of the n-type MOSFET 101, respectively.

The gate electrode can be processed with a high degree of accuracy, and a threshold voltage can be easily and correctly controlled in the CMOS semiconductor device 100. The LWR of a gate length Lg can be 5% or less.

Specific structures of the gates of the CMOS semiconductor device 100 are as follows, for example.

n-type MOSFET: W/TiN/MgO (or LaO)/HfSiON/Si substrate

p-type MOSFET: W/TiN/AlO/HfSiON/Si substrate

A method for producing the CMOS semiconductor device 100 according to the first embodiment will be described with reference to FIGS. 1A to 1K. The same reference as that in FIG. 1 represents the same or corresponding part in the drawings. The production method includes the following step 1 to step 9.

Step 1: As shown in FIG. 1A, the semiconductor substrate 105 composed of silicon is prepared. As described in FIG. 1A, the n-type MOSFET 101 is formed on the left side, and the p-type MOSFET 102 is formed on the right side. In addition, the semiconductor substrate 105 is omitted after FIG. 1B.

Then, a silicon oxide film (not shown) having a film thickness of 1 nm or less is formed on the semiconductor substrate 105, and then an insulation layer 1 is formed thereon. The insulation layer 1 is composed of a high-k (high-dielectric) material such as HfSiON. The insulation layer 1 is formed by an ALD method, a MOCVD method, a sputtering method, or the like. According to need, a nitriding treatment or a heat treatment may be performed in the middle of or after this process.

The cap layer 22 composed of Al₂O₃ is formed on the insulation layer 1. The cap layer 22 is about 1 nm in thickness, and made by the ALD method, the MOCVD method, the sputtering method, or the like. According to need, a heat treatment may be performed.

Then, a first TiN layer 31 is formed to be about 10 nm in thickness on the cap layer 22, and then a SiN layer 33 is formed to be about 10 nm in thickness. These are formed by the sputtering method, a CVD method, or the like.

Step 2: As shown in FIG. 1B, the SiN layer 33 in an n-MOSFET formation region is removed by dry etching using a photoresist (not shown) as an etching mask, for example. Then, the photoresist mask is removed, and the first TiN layer 31 and the cap layer 22 are removed by wet etching with H₂O₂, using the SiN layer 33 as an etching mask. The insulation layer 1 is hardly damaged through the above steps.

Then, the cap layer 12 composed of MgO or LaO is formed by the ALD method, the MOCVD method or the sputtering method, for example. The film thickness of the cap layer 12 is about 1 nm, but this is not necessarily the same as that of the cap layer 22 in a p-MOSFET formation region.

In addition, a Hf layer may be further formed on the cap layers 12 and 22. In this case, the gate insulation layer has a structure of HfO/MgO/HfSiON in the n-type MOSFET, and the gate insulation layer has a structure of HfO/AlO/HfSiON in the p-type MOSFET.

Step 3: As shown in FIG. 1C, a second TiN layer 32 is formed to be about 10 nm in thickness by the sputtering method or the CVD method, for example.

In addition, although the first and second TiN layers 31 and 32 are needed in the production steps, they do not remain in a final product. Therefore, they are preferably formed of the material which can be easily formed, high in selectivity, and easily removed. For example, polycrystalline Si may be used instead of TiN.

Step 4: As shown in FIG. 1D, a SiN layer 34 is formed to be about 10 nm in thickness by the sputtering method or the CVD method, for example. Then, a resist mask 36 is formed in the n-MOSFET formation region.

Step 5: As shown in FIG. 1E, the SiN layer 34 is selectively etched using the resist mask 36 as an etching mask. The etching stops on the second TiN layer 32.

Step 6: As shown in FIG. 1F, the resist mask 36 is selectively removed by plasma ashing or the like.

Step 7: As shown in FIG. 1G, the second TiN layer 32 is selectively removed using the SiN layer 34 as an etching mask.

Step 8: As shown in FIG. 1H, the SiN layers 33 and 34 and the exposed cap layer 12 are removed by wet etching.

Step 9: As shown in FIG. 1I, the first and second TiN layers 31 and 32 are selectively removed by wet etching with H₂O₂, for example.

Step 10: As shown in FIG. 1J, a TaN layer 3 composed of a mid-gap material having high heat resistance is formed to be 30 nm or less in thickness by a sputtering method, for example. As the mid-gap material, TiN may be used instead of TaN.

Then, a low-resistance tungsten layer 4 is formed on the TaN layer 3 by a sputtering method, for example. Its film thickness is 50 nm, for example.

Step 11: Finally, as shown in FIG. 1K, the tungsten layer 4, the TiN layer 3, the cap layers 12 and 22, and the insulation layer 1 are etched using a hard mask (not shown) composed of SiN as an etching mask, whereby the gate electrode 10 of the n-type MOSFET and the gate electrode 20 of the p-type MOSFET are formed.

In the above steps, the CMOS semiconductor device 100 is formed as shown in FIG. 1K.

In addition, although not described in the above, the well region, the interlayer insulation layer, and the source/drain regions are formed by the same production steps as those of the conventional CMOS semiconductor device.

As described above, since the metal layers (the tungsten layer 4 and the TaN layer in this case) of the gate electrodes of the n-MOSFET and the p-MOSFET are made of the same material, in the steps of producing the CMOS semiconductor device 100 according to this embodiment, they can be etched in the same etching step (step 11 in this case). Therefore, a fine gate electrode having a gate length which is as small as 20 nm, for example, can be etched with a high degree of accuracy.

That is, according to the production method according to this first embodiment, since the gate metal layers for the n-type MOSFET and the p-type MOSFET are made of the same material, the controllability can be improved as compared with the case where different materials are etched at the same time.

For example, when the material of the gate metal layer is different from each other, its etched shape differs from each other, and the selectivity with the lower insulation layer (high-k material) becomes low. When the etched shape is different, a gate length and a channel length are different between the n-type MOSFET and the p-type MOSFET. In addition, when the selectivity becomes low, the semiconductor substrate 1 is also etched.

In addition, since the metal used to form the gate electrode finally is directly formed on the high-k material (insulation layer) such as HfSiON, a part of an element isolation region made of STI or the like is not etched by the etching step. Thus, preferable element isolation characteristic can be obtained.

Second Embodiment

A method for producing a CMOS semiconductor device according to a second embodiment is shown in FIGS. 2A to 2C.

According to this production method, a structure shown in FIG. 2A is provided through the same steps as those shown in FIGS. 1A to 1F.

Then, as shown in FIG. 2B, the second TiN layer 32 and the cap layer 12 are etched by selective etching using the SiN layer 34 as an etching mask.

Then, the tungsten layer 4 is formed on the whole surface by the CVD method or the sputtering method, for example.

Then, as shown in FIG. 2C, the tungsten layer 4, and the TiN layers 31 and 33 are etched using a hard mask (not shown) composed of SiN, for example, as an etching mask, whereby gate electrodes of the n-type MOSFET and the p-type MOSFET are formed.

In the above steps, a CMOS semiconductor device 150 is formed as shown in FIG. 2C.

Third Embodiment

FIGS. 3A to 3H show a method for producing a CMOS semiconductor device according to a third embodiment. The production method includes the following steps 1 to 8. According to this production method, the SiN layers 33 and 34 formed in the production method shown in FIGS. 1A to 1K in the first embodiment are not formed. In the drawings, the same references as those in FIGS. 1A to 1K show the same or corresponding parts.

Step 1: As shown in FIG. 3A, the insulation layer 1 composed of HfSiON, for example, and the cap layers 12 and 22, and TiN layers 31 and 32 are formed on the semiconductor substrate 105 (omitted after FIG. 3B). These layers are made by roughly the same steps as those in FIGS. 1A to 1C except for the step of forming the SiN layer 33.

Step 2: As shown in FIG. 3B, the photoresist mask 36 is formed in the n-MOSFET formation region.

Step 3: As shown in FIG. 3C, the TiN layer 32 is selectively removed by wet etching with H₂O₂, for example, using the resist mask 36 as an etching mask.

Step 4: As shown in FIG. 3D, the resist mask 36 is removed by an ashing method. In this step, a surface of the cap layer 12 is exposed to an ashing environment.

Step 5: As shown in FIG. 3E, the cap layer 12 on the insulation layer 1 is removed by wet etching using the TiN layers 31 and 32 as etching masks.

Step 6: As shown in FIG. 3F, the TiN layers 31 and 32 are selectively removed.

Step 7: As shown in FIG. 3G, the TaN layer 3 is formed to be 30 nm or less in thickness by a sputtering method, for example. Here, TiN may be used instead of TaN. Then, the low-resistance tungsten layer 4 is formed on the TaN layer 3 by a sputtering method, for example. Its film thickness is 50 nm, for example.

Step 8: Finally, as shown in FIG. 3H, the tungsten layer 4, the TaN layer 3, and the cap layers 12 and 22 are etched using a hard mask (not shown) composed of SiN, for example, as an etching mask, whereby the gate electrode 10 of the n-type MOSFET and the gate electrode 20 of the p-type MOSFET are formed.

According to the production method, since the SiN layer is not formed, the production steps can be simplified. Meanwhile, the surface of the cap layer 12 is exposed to the ashing environment in step 4 (FIG. 3D). Therefore, the production method is preferably used in a case where the ashing step does not affect the device characteristics.

Fourth Embodiment

FIGS. 4A to 4H show a method for producing a CMOS semiconductor device according to a fourth embodiment. The production method includes the following steps 1 to 8. In the drawings, the same references as those in FIGS. 1A to 1K show the same or corresponding parts.

Step 1: As shown in FIG. 4A, the insulation layer 1 composed of HfSiON is formed on a semiconductor substrate (not shown) and then an amorphous silicon layer 40 is formed by the CVD method or the like thereon.

Step 2: As shown in FIG. 4B, a photoresist layer 51 is formed in the n-type MOSFET formation region. Then, Al ions 41 are implanted into the amorphous silicon layer 40 in the p-type MOSFET formation region using the photoresist layer 51 as an implantation mask.

Step 3: As shown in FIG. 4C, the photoresist layer 51 is removed and then a photoresist layer 52 is formed in the p-type MOSFET formation region. Then, Mg ions 42 are implanted into the amorphous silicon layer 40 in the n-type MOSFET formation region, using the photoresist layer 52 as an implantation mask.

Step 4: As shown in FIG. 4D, the photoresist layer 52 is removed. Thus, the Mg ions are implanted in the n-type MOSFET formation region of the amorphous silicon layer 40 and the Al ions are implanted in the p-type MOSFET formation region thereof.

Step 5: As shown in FIG. 4E, a heat treatment is performed to segregate Mg and Al at an upper part and a lower part of the amorphous silicon layer 40. The heat treatment is performed at a processing temperature of 600° C. for a processing time of 30 seconds by a RTA method, for example. As a result, as shown in FIG. 4E, Mg segregated layers 45 and 46 are formed on the lower and upper parts of the amorphous silicon layer 40 in the n-type MOSFET formation region, and Al segregated layers 43 and 44 are formed on the lower and upper parts of the amorphous silicon layer 40 in the p-type MOSFET formation region.

Step 6: As shown in FIG. 4F, the Mg segregated layer 46, the Al segregated layer 44, and the amorphous silicon layer 40 are removed by wet etching with a KOH aqueous solution, for example.

Step 7: As shown in FIG. 4G, the Mg segregated layer 45 and the Al segregated layer 43 are oxidized by plasma oxidization with oxygen plasma, whereby the cap layer 12 composed of MgO and the cap layer 22 composed of AlO are formed.

Step 8: As shown in FIG. 4H, the TiN layer 3 and the tungsten layer 4 are sequentially formed.

Finally, in the same step as step 11 (FIG. 1K) in the first embodiment, the TiN layer 3 and the tungsten layer 4 are etched at the same time, and the cap layers 12 and 22, and the insulation layer 1 are etched, whereby the gate electrodes are formed.

FIGS. 5A to 5C show a method for producing another CMOS semiconductor device according to the fourth embodiment.

According to this production method, after step 5 (FIG. 4E), only the Mg segregated layer 46 and the Al segregated layer 44 formed on the upper part of the amorphous silicon layer 40 are etched, and the amorphous silicon layer 40 remains.

Then, as shown in FIG. 5B, the amorphous silicon layers 40 in the n-type MOSFET formation region and the p-type MOSFET formation region are etched at the same time using a resist mask (not shown), for example. In addition, the Mg segregated layer 44, the Al segregated layer 43, and the insulation layer 1 are etched, whereby gate electrodes are formed.

Finally, a gate metal 48 composed of NiSi is formed by a reaction between amorphous silicon and nickel, using a step of producing a FUSI gate.

As described above, according to the production method according to the fourth embodiment, since the amorphous silicon layer is etched to form the gate electrodes of the n-type MOSFET formation region and the p-type MOSFET formation region at the same time, the process can be performed with a high degree of accuracy.

Fifth Embodiment

FIGS. 6A to 6H show a method for producing a CMOS semiconductor device according to a fifth embodiment. The production method includes the following steps 1 to 8. In the drawings, the same references as those in FIGS. 1A to 1K show the same or corresponding parts.

Step 1: As shown in FIG. 6A, the insulation layer 1 composed of HfSiON is formed on a semiconductor substrate (not shown) and then an amorphous silicon layer 60 is formed by the CVD method or the like.

Step 2: As shown in FIG. 6B, a TEOS (or SiN) layer 55 is formed in the n-type MOSFET formation region. Then, an Al layer 43 and an amorphous silicon layer 61 are formed by the sputtering method or the CVD method.

Step 3: As shown in FIG. 6C, a heat treatment is performed to diffuse Al, and the Al layer 43 is formed on a surface of a polycrystalline silicon layer 63 and on the insulation layer 1. In addition, in the heat treatment step, the amorphous silicon layer 61 becomes the polycrystalline silicon layer 63.

Step 4: As shown in FIG. 6D, the polycrystalline silicon layer 63 and the Al layer 43 are removed, so that the Al layer 43 remains only on the insulation layer 1 in the p-type MOSFET formation region.

Step 5: As shown in FIG. 6E, the TEOS layer 55 is removed. Then, a TEOS layer 56 is formed in the p-type MOSFET formation region. Then, an Mg layer 44 and an amorphous silicon layer 64 are formed by the sputtering method or the CVD method.

Step 6: As shown in FIG. 6F, a heat treatment is performed to diffuse Mg, and the Mg layer 44 is formed on a surface of a polycrystalline silicon layer 65 and on the insulation layer 1. In addition, in the heat treatment step, the amorphous silicon layer 64 becomes the polycrystalline silicon layer 65.

Step 7: As shown in FIG. 6G, the layers formed above the polycrystalline silicon layer 62 are all removed. Thus, there remain the insulation layer 1, the Mg layer 44 formed on the insulation layer 1 in the n-type MOSFET formation region, and the Al layer 43 formed on the insulation layer in the p-type MOSFET formation region. In addition, plasma oxidation is performed with oxygen plasma, so that the cap layer 12 composed of MgO and the cap layer 22 composed of AlO are formed.

Step 8: As shown in FIG. 6H, the TiN layer 3 and the tungsten layer 4 are sequentially formed.

Finally, in the same step as step 11 (FIG. 1K) in the first embodiment, the TiN layer 3 and the tungsten layer 4 are etched at the same time, and then the cap layers 12 and 22, and the insulation layer 1 are etched, whereby gate electrodes are formed.

As described above, according to the production method according to the fifth embodiment, since the gate electrodes of the n-type MOSFET formation region and the p-type MOSFET formation region are formed at the same time, the processing can be implemented with a high degree of accuracy.

Sixth Embodiment

FIGS. 7A to 7F show a method for producing a CMOS semiconductor device according to a sixth embodiment. The production method includes the following steps 1 to 6. In the drawings, the same references as those in FIGS. 1A to 1K show the same or corresponding parts.

Step 1: As shown in FIG. 7A, a dielectric body composed of HfSiON or the like, and a polycrystalline silicon layer are laminated on the semiconductor substrate (not shown) composed of silicon, for example. Then, these are etched at the same time to form a gate electrode composed of the insulation layer 1 and a polycrystalline silicon layer 70 in each of the n-type MOSFET formation region and the p-type MOSFET formation region.

Since a gate metal of each gate electrode is composed of the polycrystalline silicon layer 70, the high-accuracy processing can be implemented by one etching step. For example, a gate length of the gate electrode is about 20 μm.

Step 2: As shown in FIG. 7B, a silicon oxide layer is formed on the whole surface by the CVD method, for example. Then, an upper surface is flattened by a CMP method, and an interlayer insulation layer 71 is formed.

Step 3: As shown in FIG. 7C, a mask 72 (not shown in FIG. 7C) is formed in the p-type MOSFET formation region, and the polycrystalline silicon 70 in the n-type MOSFET formation region is selectively removed.

Step 4: As shown in FIG. 7D, a cap layer 73 composed of MgO, for example, a TaSiN layer 74, and a tungsten layer 75 are sequentially formed on the mask 72. These layers are formed by the ALD method, or the MOCVD method, for example.

Step 5: As shown in FIG. 7E, the cap layer 73, the TaSiN layer 74, and the tungsten layer 75 are etched from the above. Then, a mask (not shown) is formed on the n-type MOSFET, and the polycrystalline silicon 70 of the p-type MOSFET is selectively etched. Then, a cap layer 76 composed of AlO, a Pt layer 77, and the tungsten layer 75 are formed.

Step 6: As shown in FIG. 7F, after flattening the surface by the CMP method, the interlayer insulation layer 71 is removed, and a gate electrode (replacement gate) is formed in each of the n-type MOSFET formation region and the p-type MOSFET formation region.

When this production method is used, the metal material having low heat resistance can be selected as the gate metal material, so that a range of options to choose materials can be expanded.

In addition, when the control of the threshold voltage is not sufficient only by selecting the high-k material, the threshold voltage can be adjusted by appropriately selecting a material of the gate metal.

Seventh Embodiment

According to the above embodiments 1 to 6, as shown in FIG. 9, the gate electrode of the n-type MOSFET and the gate electrode of the p-type MOSFET each have the insulation layer made of the common high-k material such as HfSiON, and the cap layer made of the different material such as nCap composed of LaO or MgO, for example, or pCap composed of AlO, for example. Thus, the threshold voltage is correctly controlled.

In addition, the metal layer (metal) formed on the cap layer is made of the same material in each gate electrode.

Alternatively, the gate electrodes of the n-type MOSFET and the p-type MOSFET may only have the same metal layer (metal) and have different insulation layers (n-high-k and p-high-k).

For example, even when produced to have the structure as shown in FIG. 9, they finally have the structure as shown in FIG. 8 in some cases because the insulation layers composed of the common high-k materials react with the cap layers thereon by the heat treatment in the manufacturing step.

Specifically, the gate electrodes have the following stacked structures.

n-type MOSFET: W/TiN/HfMgO/Si substrate

p-type MOSFET: W/TiN/HfAlO/Si substrate

These structures are different from that in FIG. 9 in that the gate insulation layers have a two-layer structure instead of the one-layer structure.

In addition, as another structure, the gate electrodes may have the following structures.

n-type MOSFET: W/TiN/MgO/AlO/HfSiON/Si substrate

p-type MOSFET: W/TiN/AlO/MgO/HfSiON/Si substrate

Thus, the cap layer may have a two-layer structure. In addition, AlO and MgO may be exchanged in a vertical direction.

In addition, an additional cap layer may be inserted to only one of the n-type MOSFET and the p-type MOSFET. In this case, the gate electrodes have the following stacked structures.

n-type MOSFET: W/TiN/MgO/HfSiON/Si substrate

p-type MOSFET: W/TiN//HfSiON/Si substrate

Alternatively, SiO₂ or SiON is provided on the Si substrate, the cap layer is provided thereon, and the insulation layer composed of the high-k material such as HfSiON is provided thereon as follows.

n-type MOSFET: W/TiN/HfSiON/MgO/SiO₂ (SiON)/Si substrate

p-type MOSFET: W/TiN/HfSiON/AlO/SiO₂ (SiON)/Si substrate

In this case, in the case where a vertical relationship of the insulation layer and the cap layer is reversed, the cap layer composed of MgO or AlO can be arranged at a position close to the Si substrate. As a result, the threshold voltage can be controlled more easily.

Eighth Embodiment

After etching the gate electrode under the condition that both gate metals are composed of polycrystalline silicon as shown in FIG. 10A, a final structure may become as shown in FIG. 10B due to a reaction between polycrystalline silicon and Ni or Pt.

That is, the present invention is characterized in that since the gate electrodes of the n-type MOSFET and the p-type MOSFET are composed of the same gate metal, these gate electrodes can be formed at the same time in one etching step, so that the etching process can be performed with a very high degree of accuracy.

Therefore, as shown in FIG. 10A and FIG. 10B, after etching the gate metal, the materials of the gate metals may be different between the n-type MOSFET and the p-type MOSFET.

Specifically, the stacks at the time of etching of the gate electrode is as follows.

n-type MOSFET: Poly-Si/MgO/HfSiO/Si substrate

p-type MOSFET: Poly-Si/AlO/HfSiON/Si substrate

Then, the stacks of the final structure is as follows.

n-type MOSFET: FUSI/NiSi/MgO/HfSiO/Si substrate

p-type MOSFET: FUSI-PtSi/AlO/HfSiO/Si substrate

In addition, while the gate electrode structure has been mainly described in this embodiment, the other structures such as the source/drain are the same as those of the CMOS semiconductor device 100 shown in FIG. 1. Furthermore, a HALO layer or an extension layer may be formed according to need.

Ninth Embodiment

FIG. 11 is a schematic view of a CMOS semiconductor device according to a ninth embodiment.

The CMOSFET has three kinds of structures as gate electrodes of n-type CMOSFETs as follows.

n-type MOSFET1: Poly-SI/TiN/LaO/HfSiO/Si substrate

n-type MOSFET2: Poly-SI/TiN/HfSiO/Si substrate

n-type MOSFET3: Poly-SI/TiN/AlO/HfSiO/Si substrate

In addition, while a SiO₂ film is provided on the surface of the Si substrate in FIG. 11, it may be omitted.

As for the n-type MOSFETs 1 to 3, threshold voltages (Vth) are shifted to +0.2V (MOSFET1), +0.5V (MOSFET2), and +0.8V (MOSFET3) as compared with the structure in which the gate insulation layer is only composed of SiO₂.

On the other hand, three kinds of structures are used for gate electrodes of p-type CMOSFETs as follows.

p-type MOSFET1: Poly-SI/TiN/LaO/HfSiO/Si substrate

p-type MOSFET2: Poly-SI/TiN/HfSiO/Si substrate

p-type MOSFET3: Poly-SI/TiN/AlO/HfSiO/Si substrate

As for the p-type MOSFETs 1 to 3, threshold voltages (Vth) are shifted to −0.2V (MOSFET1), −0.5V (MOSFET2), and −0.8V (MOSFET3) as compared with the structure in which the gate insulation layer is only composed of SiO₂.

Since these gate electrodes are each formed of the same gate metal material, they can be made through only one etching step, so that the gate electrode can be high in processing accuracy.

In addition, three kinds of gate electrodes having different shift amounts of the threshold voltages are provided in each of the n-type and p-type MOSFETs. Therefore, an integrated CMOS semiconductor device containing a plurality of MOSFETs having different threshold voltages can be produced by combining the six kinds of gate electrodes. 

1. A CMOS semiconductor device having an n-type MOSFET and a p-type MOSFET, comprising: a gate electrode of the n-type MOSFET having a first insulation layer composed of a high-k material, and a first metal layer provided on the first insulation layer and composed of a metal material; and a gate electrode of the p-type MOSFET having a second insulation layer composed of a high-k material, and a second metal layer provided on the second insulation layer and composed of a metal material, wherein the first insulation layer and the second insulation layer are composed of the different high-k materials, and the first metal layer and the second metal layer are composed of the same metal material.
 2. The CMOS semiconductor device according to claim 1, wherein the first insulation layer is composed of the high-k material containing an element which is not contained in the second insulation layer, and the second insulation layer is composed of the high-k material containing an element which is not contained in the first insulation layer.
 3. The CMOS semiconductor device according to claim 1 or 2, wherein the first insulation layer and the second insulation layer are each composed of the high-k material containing three or more kinds of elements in which only one kind is different from all the others and the others are the same.
 4. The CMOS semiconductor device according to any one of claims 1 to 3, wherein the first insulation layer is composed of HfLaO or HfMgO, and the second insulation layer is composed of HfAlO.
 5. A CMOS semiconductor device having an n-type MOSFET and a p-type MOSFET, comprising: a gate electrode of the n-type MOSFET having a first insulation layer containing a high-k material and a cap material, and a first metal layer provided on the first insulation layer and composed of a metal material; and a gate electrode of the p-type MOSFET having a second insulation layer containing a high-k material and a cap material, and a second metal layer provided on the second insulation layer and composed of a metal material, wherein the first insulation layer and the second insulation layer are each composed of the same high-k material and the cap materials different from one another, and the first metal layer and the second metal layer are composed of the same metal material.
 6. The CMOS semiconductor device according to claim 5, wherein the first insulation layer is composed of a common high-k material layer formed on a surface of a semiconductor substrate, and a first cap material layer formed thereon, the second insulation layer is composed of a common high-k material layer formed on the surface of the semiconductor substrate, and a second cap material layer formed thereon, and the first cap material layer or the second cap material layer covers the semiconductor substrate positioned between the gate electrode of the n-type MOSFET and the gate electrode of the p-type MOSFET.
 7. The CMOS semiconductor device according to claim 5 or 6, wherein the first insulation layer comprises the high-k material layer composed of HfO₂, HfSiO or its nitride, and the cap material layer composed of LaO or MgO, and the second insulation layer comprises the high-k material layer composed of HfO₂, HfSiO or its nitride, and the cap material layer composed of AlO.
 8. The CMOS semiconductor device according to any one of claims 1 to 7, wherein the first metal layer and the second metal layer are each composed of one material selected from a group including TiN, TaN, TaSiN, NiSi, PtSi, and CoSi₂.
 9. A method for producing a CMOS semiconductor device having an n-type MOSFET and a p-type MOSFET, comprising the steps of: preparing a semiconductor substrate defined by an n-type MOSFET formation region and a p-type MOSFET formation region; forming a high-k material layer, a first cap layer, and a first metal layer sequentially on the semiconductor substrate; removing the first cap layer and the first metal layer except for those in the p-type MOSFET formation region; forming a second cap layer and a second metal layer sequentially on the semiconductor substrate; removing the second metal layer except for that in the n-type MOSFET formation region; removing the second cap layer provided between the n-type MOSFET formation region and the p-type MOSFET formation region, using the first metal layer and the second metal layer as masks; removing the first metal layer and the second metal layer; forming a gate metal material layer on the semiconductor substrate; and forming a gate metal layer of a gate electrode of each of the n-type MOSFET and the p-type MOSFET by etching the gate metal material layer in the same etching step.
 10. A method for producing a CMOS semiconductor device having an n-type MOSFET and a p-type MOSFET, comprising the steps of: preparing a semiconductor substrate defined by an n-type MOSFET formation region and a p-type MOSFET formation region; forming a high-k material layer, a first cap layer, a first metal layer, and a first silicon insulation layer sequentially on the semiconductor substrate; removing the first cap layer, the first metal layer, and the first silicon insulation layer except for those in the p-type MOSFET formation region; forming a second cap layer, a second metal layer, and a second silicon insulation layer sequentially on the semiconductor substrate; removing the second metal layer and the second silicon insulation layer except for those in the n-type MOSFET formation region; removing the second cap layer provided between the n-type MOSFET formation region and the p-type MOSFET formation region, using the first silicon insulation layer and the second silicon insulation layer as masks; removing the first silicon insulation layer and the second silicon insulation layer; removing the first metal layer and the second metal layer; forming a gate metal material layer on the semiconductor substrate; and forming a gate metal layer of a gate electrode of each of the n-type MOSFET and the p-type MOSFET by etching the gate metal material layer in the same etching step.
 11. The method for producing a CMOS semiconductor device according to claim 9 or 10, wherein the gate metal material layer has a laminated structure of a mid-gap material layer and a low-resistance material layer.
 12. The method for producing a CMOS semiconductor device according to claim 11, wherein the mid-gap material is composed of TiN, and the low-resistance material is composed of W.
 13. A method for producing a CMOS semiconductor device having an n-type MOSFET and a p-type MOSFET, comprising steps of: preparing a semiconductor substrate defined by an n-type MOSFET formation region and a p-type MOSFET formation region; forming a high-k material layer, a first cap layer, a first metal layer, and a first silicon insulation layer sequentially on the semiconductor substrate; removing the first cap layer, the first metal layer, and the first silicon insulation layer except for those in the p-type MOSFET formation region; forming a second cap layer, a second metal layer, and a second silicon insulation layer sequentially on the semiconductor substrate; removing the second metal layer and the second silicon insulation layer except for those in the n-type MOSFET formation region; removing the second cap layer formed on a side wall or an upper surface of the first metal layer and the first silicon insulation layer; removing the first silicon insulation layer and the second silicon insulation layer. removing the first metal layer and the second metal layer; forming a gate metal material layer on the semiconductor substrate; and forming a gate metal layer of a gate electrode of each of the n-type MOSFET and the p-type MOSFET by etching the gate metal material layer in the same etching step.
 14. The method for producing a CMOS semiconductor device according to any one of claims 9 to 13, wherein the first metal layer and the second metal layer are each composed of one material selected from a group including TiN, TaN, TaSiN, NiSi, PtSi, and CoSi₂.
 15. The method for producing a CMOS semiconductor device according to any one of claims 10 to 13, wherein the first silicon insulation layer and the second silicon insulation layer are each composed of silicon nitride.
 16. A method for producing a CMOS semiconductor device having an n-type MOSFET and a p-type MOSFET, comprising the steps of: preparing a semiconductor substrate defined by an n-type MOSFET formation region and a p-type MOSFET formation region; forming a high-k material layer and an amorphous silicon layer, on the semiconductor substrate; implanting first metal ions in the amorphous silicon in the p-type MOSFET formation region; implanting second metal ions in the amorphous silicon in the n-type MOSFET formation region; segregating a first segregated layer of a first metal and a second segregated layer of a second metal, in a boundary between the high-k material layer and the amorphous silicon layer by a heat treatment; removing the amorphous silicon layer; making a first cap layer and a second cap layer by oxidizing the first segregated layer and the second segregated layer; forming a gate metal material layer on the semiconductor substrate; and forming a gate metal layer of a gate electrode of each of the n-type MOSFET and the p-type MOSFET, by etching the gate metal material layer in the same etching step.
 17. A method for producing a CMOS semiconductor device having an n-type MOSFET and a p-type MOSFET, comprising the steps of: preparing a semiconductor substrate defined by an n-type MOSFET formation region and a p-type MOSFET formation region; forming a high-k material layer and a silicon layer, on the semiconductor substrate; depositing a first metal on the silicon layer in the p-type MOSFET formation region; segregating a first segregated layer of the first Metal, in a boundary between the high-k material layer and the silicon layer by a heat treatment; forming a deposit layer of a second metal, on the silicon layer in the n-type MOSFET formation region; segregating a second segregated layer of the second metal, in a boundary between the high-k material layer and the silicon layer by a heat treatment; removing the silicon layer; making a first cap layer and a second cap layer by oxidizing the first segregated layer and the second segregated layer; forming a gate metal material layer on the semiconductor substrate; and forming a gate metal layer of a gate electrode of each of the n-type MOSFET and the p-type MOSFET, by etching the gate metal material layer in the same etching step.
 18. A method for producing a CMOS semiconductor device having an n-type MOSFET and a p-type MOSFET, comprising the steps of: preparing a semiconductor substrate defined by an n-type MOSFET formation region and a p-type MOSFET formation region; forming a high-k material layer on the semiconductor substrate; forming a first cap metal layer in the n-type MOSFET formation region and a second cap metal layer in the p-type MOSFET formation region; forming a polycrystalline silicon layer on the semiconductor substrate; forming a polycrystalline silicon gate layer in each of the n-type MOSFET formation region and the p-type MOSFET formation region, by etching the polycrystalline silicon layer in the same etching step; and making the polycrystalline silicon gate layers of the n-type MOSFET formation region and the p-type MOSFET formation region into silicide metal gate layers composed of different materials.
 19. A method for producing a CMOS semiconductor device having an n-type MOSFET and a p-type MOSFET, comprising the steps of: preparing a semiconductor substrate defined by an n-type MOSFET formation region and a p-type MOSFET formation region; forming a high-k material layer and a polycrystalline silicon layer, on the semiconductor substrate; forming a polycrystalline silicon gate layer in each of the n-type MOSFET formation region and the p-type MOSFET formation region, by etching at least the polycrystalline silicon layer in the same etching step; and forming an insulation layer to cover the polycrystalline silicon gate layer, on the semiconductor substrate, and forming an interlayer insulation layer provided by reducing a film thickness of the insulation layer to expose an upper part of the polycrystalline silicon gate layer; removing the polycrystalline silicon gate in the n-type MOSFET formation region and forming a first cap layer and a gate metal layer instead; and removing the polycrystalline silicon gate in the p-type MOSFET formation region and forming a second cap layer and a gate metal layer instead. 